1/4" Nodir yer kublari/disk/uzuklar/silindrlari Samarium Cobalt SmCo 17-5 Magnit
Agar sizda qiziqarli bo'lsa, iltimos, istalgan vaqtda men bilan bog'laning.
1 dona yoki 100,{2}} magnit sotib olsangiz ham, boshqa joyda yaxshiroq xizmatni topa olmaysiz.
SmCo Disc Magnet yuqori samarali 26M Sm2Co17 dan tayyorlangan.
boshqa himoya qoplamalarsiz. Ushbu elementning o'lchami D10x6 mm
qalinligi orqali magnitlangan.
Mahsulot | 1/4" Noyob Yer kublari/Disk/halqalar/silindrlar samarium kobalt SmCo 17-5 Magnit |
Shakl | Disk / Dumaloq / Disk / Acr / silindr / blok |
Material | Samarium kobalt |
Baho | GME-Smco |
Magnitlangan | so'rov bo'yicha |
MOQ | 8000 dona |
Etakchi vaqt | 25-35 ish kuni |
Namuna | Ha |
Sertifikat | ISO2000, TS16949, RoHS, Idoralar, SGS & REACH |
To'lov | T/T, PayPal, Western Union |
Samarium Cobatl magnitlari:yaxshi termal barqarorlik, korroziyaga chidamli, demagnetizatsiyaga chidamli
Samarium-kobalt (SmCo) magniti, noyob tuproq magnitining bir turi, samarium va kobalt qotishmasidan yasalgan kuchli doimiy magnitdir.
Ular odatda neodim magnitlari bilan bir xil kuchga ega, lekin yuqori harorat ko'rsatkichlariga va yuqori majburlashga ega.
samarium-kobalt (SmCo) magnitlari mo'rt bo'lib, yorilish va parchalanishga moyil. Samarium-kobalt magnitlari maksimal energiya mahsulotlariga (BHmax) ega bo'lib, ular 16 megagauss-oersteddan (MGOe) 33 MGOe gacha, taxminan. 128 kJ/m3 dan 264 kJ/m3 gacha; ularning nazariy chegarasi 34 MGOe, taxminan 272 kJ/m3.
samarium-kobalt (SmCo) magnitlari ikkita "seriya", ya'ni 1:5 seriya va 2:17 seriyada mavjud.
Sinterlangan Samarium Cobalt magnitlari magnit anizotropiyaga ega, ya'ni ular faqat magnit yo'nalishi o'qida magnitlanishi mumkin. Bu ishlab chiqarish jarayonida materialning kristalli tuzilishini tekislash orqali amalga oshiriladi.
Ishlov berish va magnitlanish
Samarium Cobalt magnitlari demagnetizatsiyaga kuchli qarshilik ko'rsatadi. Barcha Samarium Cobalt magnitlarini an'anaviy burg'ulash, burilish yoki frezalash jarayonlari bilan hosil qilish mumkin emas va ular magnitlangan bo'lishidan oldin maydalangan bo'lishi kerak. Bundan tashqari, katta yoki murakkab yig'ilishlar odatda yig'ilishdan oldin magnitlanadi. Samarium Cobalt magnitlari uchun standart toleranslar tuproq o'lchamlari uchun +/-.005 dir.
1:5 qotishma material
1:5 16 MGOe (energiya mahsuloti) dan 22 MGOegacha taklif qiladi va taxminan 50% samarium va 50% kobaltdan iborat. 1: 5 seriyali maksimal tavsiya etilgan ish harorati 250 daraja. SmCo 1:5 magnitlari magnitlanish uchun 2:17 materiallarga qaraganda kamroq maydon kuchini talab qiladi. Ba'zi hollarda magnitlash moslamasi mavjud bo'lganda, 1: 5 material bir nechta qutblar bilan magnitlanishi mumkin.
2:17 qotishma material
2:17 24 MGOe dan 32 MGOe gacha taklif qiladi va taxminan 25% samarium, 5% mis, 18% temir, 2% gafniy yoki tsirkoniydan iborat bo'lib, qolgan qismi kobaltdir. 2:17 seriyali maksimal ish harorati 350 daraja. Bundan ham yuqori haroratlarda ishlay oladigan 2:17 maxsus navlari mavjud. SmCo 2:17 qotishma 1:5 ga qaraganda yuqori magnitlanish maydonini talab qiladi va magnitlash moslamasi mavjud bo'lsa, ba'zida bir nechta qutbli magnitlanish mumkin.
Samarium kobalt magnitlari uchun ishlash:
| Material | Baho | Qolganlik | Majburiy kuch | Intrinsik majburlash | Maksimal energiya | Zichlik | Temp Koeffitsient | Temp Koeffitsient | Cuire harorati | Maksimal ish harorati. (TW) | ||||
| (Br) | (Hcj) | (Hcb) | (BHmax) | (D) | (Br yaqinida) | (Hcj yaqinida) | (TC) | |||||||
| mT | Gs | KA/m | Oe | KA/n | Oe | KJ/m3 | MGOe | g/sm3 | %/K | %/K | ºC | ºC | ||
| SmCo 1:5 | SmCo18 | 840 | 8400 | 605 | 7600 | 1432 | 18000 | 143 | 18 | 8.1 | -0.04 | -0.3 | 750 | 250 |
| (SmPr)CO5 | SmCo20 | 890 | 8900 | 637 | 8000 | 1432 | 18000 | 159 | 20 | 8.2 | -0.04 | -0.3 | 750 | 250 |
| SmCo22 | 930 | 9300 | 637 | 8000 | 1432 | 18000 | 175 | 22 | 8.2 | -0.04 | -0.3 | 750 | 250 | |
| LTc(HM-10) | 590 | 630 | 493 | 6200 | 1430 | 1830 | 80 | 10 | 8.2 | Harorat oralig'i | %ºC | 700 | 250 | |
| 1:5 | 20-100ºC | -0.004 | ||||||||||||
| (SmGd)CO5 | 100-200ºC | -0.021 | ||||||||||||
| 200-300ºC | -0.042 | |||||||||||||
| SmCo24 | 980 | 9800 | 676 | 8500 | 1432 | 18000 | 191 | 24 | 8.3 | -0.03 | -0.2 | 800 | 280 | |
| SmCo24H | 980 | 9800 | 676 | 8500 | 1989 | 25000 | 191 | 24 | 8.3 | -0.03 | -0.2 | 800 | 280 | |
| SmCo26L | 1030 | 10300 | 398 | 5000 | 438 | 5500 | 207 | 26 | 8.3 | -0.03 | -0.2 | 800 | 300 | |
| SmCo26 | 1030 | 10300 | 716 | 9000 | 1194 | 15000 | 207 | 26 | 8.3 | -0.03 | -0.2 | 800 | 300 | |
| 2:17 Sm2 | SmCo26M | 1030 | 10300 | 716 | 9000 | 1592 | 20000 | 207 | 26 | 8.3 | -0.03 | -0.2 | 800 | 300 |
| (CoFeCUZr)17 | SmCo26H | 1030 | 10300 | 716 | 9000 | 1989 | 25000 | 207 | 26 | 8.3 | -0.03 | -0.2 | 800 | 350 |
| SmCo28 | 1070 | 10700 | 756 | 9500 | 1194 | 15000 | 223 | 28 | 8.3 | -0.03 | -0.2 | 800 | 350 | |
| SmCo28M | 1070 | 10700 | 756 | 9500 | 1592 | 20000 | 223 | 28 | 8.3 | -0.03 | -0.2 | 800 | 350 | |
| SmCo30 | 1100 | 11000 | 772 | 9700 | 1194 | 15000 | 239 | 30 | 8.3 | -0.03 | -0.2 | 800 | 350 | |
| SmCo30M | 1100 | 11000 | 772 | 9700 | 1592 | 20000 | 239 | 30 | 8.3 | -0.03 | -0.2 | 800 | 350 | |
| LTc(HMG-22) | 980 | 9800 | 715 | 9000 | 1500 | 20000 | 230 | 23 | 8.3 | Harorat oralig'i | %ºC | 840 | 300 | |
| 2:17 | -50-25ºC | 0.005 | ||||||||||||
| (SmEr)2(CoTM)17 | 20-100ºC | 0.012 | ||||||||||||
| 100-200ºC | 0.006 | |||||||||||||
| 200-300ºC | -0.025 | |||||||||||||
Xususiyatlarga quyidagilar kiradi:
Samarium kobalt magnitlari qattiq va mo'rt bo'lib, tushib qolsa, parchalanishi yoki sinishi mumkin.
Ular yuqori magnit xususiyatlarga ega
Samarium kobalt magnitlari yaxshi termal barqarorlikni ta'minlaydi
Samarium kobalt magnitlari korroziyaga chidamli
Demagnetizatsiyaga chidamli samarium kobalt magnitlari
Afzalliklari:
Demagnetizatsiyaga juda chidamli
yuqori harorat barqarorligi (maksimal ish harorati 250 daraja (523 K) va 550 daraja (823 K); Kyuri harorati 700 darajadan (973 K) 800 darajagacha (1070 K)
Qimmat va narxlarning o'zgarishiga bog'liq (kobalt bozor narxiga sezgir)
Kamchiliklari:
Samarium kobalt magnitlari osongina chipga tushishi mumkin; ular bilan ishlashda ko'zni himoya qilish kerak.
Magnitlarni bir-biriga yopishib olishiga ruxsat berish magnitlarning parchalanishiga olib kelishi mumkin, bu esa potentsial xavf tug'dirishi mumkin.
Samarium-kobalt sinterlash deb ataladigan jarayon orqali ishlab chiqariladi va barcha sinterlangan materiallarda bo'lgani kabi, o'ziga xos yoriqlar juda mumkin. Ushbu magnitlar mexanik yaxlitlikka ega emas; Buning o'rniga magnit o'zining magnit funktsiyalari uchun ishlatilishi kerak va boshqa mexanik tizimlar tizimning mexanik ishonchliligini ta'minlash uchun mo'ljallangan bo'lishi kerak.
Neodimiy va samarium kobalti o'rtasidagi taqqoslash
| Mulk | Neodimiy | Sm-Co |
| Qolganlik (T) | 1-1.3 | 0.82-1.16 |
| Majburiylik (MA/m) | 0.875-1.99 | 0.493-1.59 |
| Nisbiy o'tkazuvchanlik | 1.05 | 1.05 |
| Remanentlik harorat koeffitsienti (%/K) | 0.12 | 0.03 |
| Haroratli majburlash koeffitsienti (%/K) | 0.55..-0.65 | 0.15..-0.30 |
| Kyuri harorati (daraja) | 320 | 800 |
| Zichlik (g/sm3) | 7.3-7.5 | 8.2-8.4 |
| CTE, magnitlanish yo'nalishi (1/K) | 5.2×106 | 5.2×106 |
| CTE, normaldan magnitlanish yo'nalishi (1/K) | 0.8×106 | 11×106 |
| Bukilish kuchi (N/mm2) | 250 | 150 |
| Siqilish kuchi (N/mm2) | 1100 | 800 |
| Kuchlanish kuchi (N/mm2) | 75 | 35 |
| Vickers qattiqligi (HV) | 550-650 | 500-650 |
| Elektr qarshiligi (Ō·sm) | (110-170)×106 | 86×106 |
Ishlab chiqarish usullari
SmCo magnitlari quyidagi shakllarda ishlab chiqariladi:
Sinterlangan - nozik SmCo kukuni qolipda siqiladi va keyin sinterlanadi, kukunni qattiq materialga birlashtiradi. Bosishning ikkita shakli mavjud: qolipli presslash (bu kukun solingan va keyin bosiladigan qattiq qolipni o'z ichiga oladi) va izostatik presslash (maxsus "rezina" matritsani o'z ichiga olgan holda, unga kukun solinadi va keyin hamma joyda teng kuch bilan bosiladi. kukun bo'yicha ko'rsatmalar). Qattiq bosilgan qismlar izostatik bosilgan qismlarga qaraganda kichikroq. Izostatik bosilgan qismlarning magnit xususiyatlari yuqoriroq bo'lsa-da, magnit xususiyatlarning bir xilligi odatda matritsa bosilgan qismlarga qaraganda past bo'ladi. Yakuniy toleranslarni qondirish uchun sinterlangan qismlar odatda ishlov berishni talab qiladi.
Compression Bonded - bu SmCo kukunining maxsus shakli plastik tashuvchi material bilan aralashtiriladi, presslanadi va keyin isitiladi. Shu tarzda tayyorlangan qismlar murakkab shaklga ega bo'lishi mumkin va asbobdan yaqin toleranslar bilan ajralib turadi, bu esa boshqa ishlov berishni talab qilmaydi. Ular sinterlangan materiallarga qaraganda kamroq energiya mahsulotiga ega - hozirda 15 MGOe oralig'ida.
Issiq teglar: 1/4 nodir tuproq kublari/disk/uzuklar/silindrlari samarium kobalt smco 17-5 magnit, Xitoy, zavod, ishlab chiqaruvchilar, yetkazib beruvchi, ulgurji savdo